Abstract
Carbon aerogel was obtained by pyrolysis of organic aerogel by ambient pressure drying technique. The effect of pyrolysis conditions on characteristics of carbon aerogel such as density, specific surface area and conductivity was studied. The properties and structure of carbon aerogel samples were investigated by nitrogen adsorption, four-point probe method and XRD diffraction. The results showed that carbon aerogel had structure between amorphous and graphite state. The highest specific surface area was 800 m2/g at pyrolysis temperature of 700oC. The pore-size was distributed in microporous, with the maximum total pore volume of 0.44 cm3/g. The electrical conductivity of carbon aerogel was highest at pyrolysis temperature of 800-900oC with the value in the range of 1.744-1.923 S/cm.
Issue: Vol 19 No 3 (2016)
Page No.: 88-95
Published: Sep 30, 2016
Section: Engineering and Technology - Research article
DOI: https://doi.org/10.32508/stdj.v19i3.572
Copyright: The Authors. This is an open access article distributed under the terms of the Creative Commons Attribution License CC-BY 4.0., which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Download PDF = 836 times
Total = 836 times
Most read articles by the same author(s)
- Duyen Khac Le, Nghiep Quoc Pham, Kien Anh Le, Capacitive deionization (CDI) for desalisation using carbon aerogel electrodes , Science and Technology Development Journal: Vol 19 No 3 (2016)